High temperature corrosion and protection of materials 7 : selected, peer reviewed papers from 7th International Symposium on High Temperature Corrosion and Protection of Materials, Les Embiez, France, May 18-23, 2008 /

Volume is indexed by Thomson Reuters CPCI-S (WoS). This special volume addresses fundamental and practical aspects of high-temperature corrosion and protection. It stresses that devoting attention to an understanding of the corrosion problems encountered by contemporary industry, and providing oppor...

Descripción completa

Detalles Bibliográficos
Clasificación:Libro Electrónico
Autores Corporativos: International Symposium on High Temperature Corrosion and Protection of Materials Les Embiez, France, European Federation of Corrosion
Otros Autores: Steinmetz, Pierre
Formato: Electrónico Congresos, conferencias eBook
Idioma:Inglés
Publicado: Uetikon-Zuerich, Switzerland ; Enfield, NH, USA : Distributed in the Americas by Trans Tech Publications, ©2008.
Colección:Materials science forum ; v. 595-598.
Temas:
Acceso en línea:Texto completo

MARC

LEADER 00000cam a2200000 a 4500
001 KNOVEL_ocn319430153
003 OCoLC
005 20231027140348.0
006 m o d
007 cr cnu---unuuu
008 090427s2008 sz a ob 101 0 eng d
040 |a NRC  |b eng  |e pn  |c NRC  |d CUS  |d VLB  |d KNOVL  |d N$T  |d KNOVL  |d OCLCF  |d KNOVL  |d YDXCP  |d E7B  |d COO  |d EBLCP  |d DEBSZ  |d OCLCQ  |d OCL  |d OCLCQ  |d STF  |d OCLCQ  |d NJR  |d OCLCQ  |d CEF  |d RRP  |d WYU  |d OCLCQ  |d TTECH  |d HS0  |d OCLCA  |d OCLCO  |d OCLCQ 
019 |a 865822936  |a 1227632748 
020 |a 9783038131663  |q (electronic bk.) 
020 |a 3038131660  |q (electronic bk.) 
020 |a 1613447183 
020 |a 9781613447185 
029 1 |a AU@  |b 000049162669 
029 1 |a DEBSZ  |b 431839379 
029 1 |a GBVCP  |b 871532042 
029 1 |a NZ1  |b 14537535 
035 |a (OCoLC)319430153  |z (OCoLC)865822936  |z (OCoLC)1227632748 
050 4 |a TA417.7.H55  |b I58 2008eb 
072 7 |a SCI  |x 050000  |2 bisacsh 
082 0 4 |a 620.11217  |2 23 
049 |a UAMI 
111 2 |a International Symposium on High Temperature Corrosion and Protection of Materials  |n (7th :  |d 2008 :  |c Les Embiez, France) 
245 1 0 |a High temperature corrosion and protection of materials 7 :  |b selected, peer reviewed papers from 7th International Symposium on High Temperature Corrosion and Protection of Materials, Les Embiez, France, May 18-23, 2008 /  |c edited by Pierre Steinmetz [and others] ; under the auspices of the European Federation of Corrosion. 
246 3 0 |a High temperature corrosion and protection of materials seven 
260 |a Uetikon-Zuerich, Switzerland ;  |a Enfield, NH, USA :  |b Distributed in the Americas by Trans Tech Publications,  |c ©2008. 
300 |a 1 online resource (2 volumes) :  |b illustrations 
336 |a text  |b txt  |2 rdacontent 
337 |a computer  |b c  |2 rdamedia 
338 |a online resource  |b cr  |2 rdacarrier 
490 1 |a Materials science forum,  |x 0255-5476 ;  |v v. 595-598 
504 |a Includes bibliographical references and indexes. 
588 0 |a Print version record. 
520 |a Volume is indexed by Thomson Reuters CPCI-S (WoS). This special volume addresses fundamental and practical aspects of high-temperature corrosion and protection. It stresses that devoting attention to an understanding of the corrosion problems encountered by contemporary industry, and providing opportunities for extended interaction, could lead to approaches for improving the performance of materials and protective measures. The book is divided into the topics: I. Materials and Coatings for Gas Turbines, II. Power Boilers and Incinerators; H2 Syngas and Biofuel Production, III. HT Materials for Nuclear Processes, IV. HT Corrosion in the Processing Industries, V. HT Corrosion of Functional Materials and Coatings, VI. Fundamentals. The 131 papers covered all aspects of the development, testing and determination of mechanisms of the degradation of coatings. Continued efforts aimed at understanding the mechanisms of formation, growth and failure of protective scales (including approaches to modelling) were another major area of interest, and accounted for nearly a quarter of the papers. A further 20% of the papers are concerned with materials issues linked to current trends in power generation: specifically, oxidation in steam/water vapor, the effects of firing biomass, the use of oxy-fuel conditions, and materials issues associated with nuclear power generation. Overall, the ratio of papers addressing practical problems, to those concerned more with fundamental aspects, was approximately 2:1; which was a good reflection on the intent of the original plan. Proceedings of an international symposium held in Les Embiez, France, in May 2008, addressing fundamental and practical aspects of high- temperature (HT) corrosion and protection of materials. The two-volume set features 131 contributions organized into six sections. The first, on materials and coatings for gas turbines, examines lifetime issues, modes of failure, oxidation and hot corrosion, and trends and developments. Articles in the second section-power boilers and incinerators, H2 singas and biofuels production-deal with advanced steam conditions, fireside corrosion, oxy-firing, use of alternative fuels, gasification, high-temperature electrolysis, and thermochemical processes. The third section, HT materials for nuclear processes, addresses various types of reactors-pressurized-water, European pressured, high-temperature, very high-temperature, and fusion-supercritical water-cooled processes, and molten metals and salts. The fourth, HT corrosion in the process industries, focuses on the steel industry, electrometallurgy, glass and ceramics production, refining, and the petrochemical and chemical industries. The fifth, HT corrosion of functional materials and coatings, examines materials for automotive applications, burners, filters, and fuel cells. The final section on fundamentals addresses various mechanisms and new techniques for measurement and characterization of corrosion. 
505 0 |a High Temperature Corrosion and Protection of Materials 7; Committees; Preface; Table of Contents; Progress in the Study of the Theory and Practice of High Temperature Protective Coatings in the 22 Years of the Les Embiez Symposia; I. Materials and Coatings for Gas Turbines; Erosion and High Temperature Oxidation Resistance of New Coatings Fabricated by a Sol-Gel Route for a TBC Application; Evolution of Oxide Scales on Aluminide Coatings under Isothermal and Cyclic Conditions; Improvement of High-Temperature Oxidation of Titanium Alloys by Dipping in a Phosphoric Acid Solution 
505 8 |a Development of a NiW In Situ Diffusion Barrier on a Fourth Generation Nickel-Base SuperalloyEffect of Material and Environmental Parameters on the Microstructure Evolution and Oxidation Behavior of a Ni-Based Superalloy Coated with a Pt-Modified Ni-Aluminide; Elaboration of Nickel Aluminide Diffusion Coatings: Application to Oxidation Resistance; Rumpling of Platinum Modified Aluminide Coatings during Thermomechanical Testing; The Kinetics of Oxidation of Ru-Bearing Nickel-Based Superalloys 
505 8 |a Platinum Diffusion and Microstructure Change in a Single Crystal Superalloy and Nickel-Based Model Alloys at 1000°CComparison of the Thermal Cycling Performance of Thermal Barrier Coatings under Isothermal and Heat Flux Conditions; Influence of Micro-Structure on Oxidation Behavior of a Ni-Based Superalloy at 1000°C ; Short-Time Oxidation of a NiAl(Zr) Bond Coat Thermochemically Deposited on a Nickel-Based Superalloy; Oxide Spallation in Beta-NiAl Coated Systems under Mechanicalloading ; Creep Deformation / Oxidation Behavior of Re-Cr-Ni Diffusion Barrier Coated Hastelloy-X at 970°C in Air 
505 8 |a Numerical Modelling of Diffusion Coupled with Cyclic Oxidation. Application to Alumina-Forming Coatings Used for Industrial Gas Turbine BladesChemistry of Ash-Deposits on Gas Turbines Hot Parts: Reactivity of Nickel, Zinc and Iron Oxides in (Na, V, S) Molten Salts; Hydrogen Detection in Buried Layers of Thermal Barrier Coatings; Aluminide Coating Formation on Internal Passages of GTD-111 Superalloy by Slurry Technique; Enigmatic Moisture Effects on Al2O3 Scale and TBC Adhesion; Phase Field Modeling of Interdiffusion Microstructure in Ni-Cr-Al Diffusion Couples 
546 |a English. 
590 |a Knovel  |b ACADEMIC - Metals & Metallurgy 
650 0 |a Materials at high temperatures  |x Corrosion  |v Congresses. 
650 0 |a Materials at high temperatures  |x Protection  |v Congresses. 
650 6 |a Matériaux à hautes températures  |x Corrosion  |v Congrès. 
650 6 |a Matériaux à hautes températures  |x Protection  |v Congrès. 
650 7 |a SCIENCE  |x Nanoscience.  |2 bisacsh 
650 7 |a Materials at high temperatures  |x Corrosion.  |2 fast  |0 (OCoLC)fst01011905 
650 7 |a Materials at high temperatures  |x Protection.  |2 fast  |0 (OCoLC)fst01011909 
655 7 |a Conference papers and proceedings.  |2 fast  |0 (OCoLC)fst01423772 
700 1 |a Steinmetz, Pierre. 
710 2 |a European Federation of Corrosion. 
776 0 8 |i Print version:  |a International Symposium on High Temperature Corrosion and Protection of Materials (7th : 2008 : Les Embiez, France).  |t High temperature corrosion and protection of materials 7.  |d Uetikon-Zuerich, Switzerland ; Enfield, NH, USA : Distributed in the Americas by Trans Tech Publications, ©2008  |z 9780878493661  |w (DLC) 2009417547  |w (OCoLC)288956294 
830 0 |a Materials science forum ;  |v v. 595-598. 
856 4 0 |u https://appknovel.uam.elogim.com/kn/resources/kpHTCPM001/toc  |z Texto completo 
938 |a ProQuest Ebook Central  |b EBLB  |n EBL1869180 
938 |a ebrary  |b EBRY  |n ebr10814209 
938 |a EBSCOhost  |b EBSC  |n 512865 
938 |a Trans Tech Publications, Ltd  |b TRAN  |n 10.4028/www.scientific.net/MSF.595-598 
938 |a YBP Library Services  |b YANK  |n 9965815 
994 |a 92  |b IZTAP