Contribution of metallography to production problem solutions II : 14th Conference "Contribution of Metallography to Production Problem Solutions" (14th CCMPPS 2017) /
| Clasificación: | Libro Electrónico |
|---|---|
| Autor Corporativo: | |
| Otros Autores: | |
| Formato: | Electrónico Congresos, conferencias eBook |
| Idioma: | Inglés |
| Publicado: |
Zurich, Switzerland :
Trans Tech Publications Ltd.,
[2017]
|
| Temas: | |
| Acceso en línea: | Texto completo |
Tabla de Contenidos:
- Intro; Contribution of Metallography to Production Problem Solutions II; Preface, Committee; Table of Contents; Chapter 1: Degradation of Materials and Failure Analysis; Using Fractography for Determining of Technological Reasons of Defect and Brittle Fractures Occurrence in Steels; The Analysis of Causes of Pressure Bottles Heads Destruction; Material Analysis of the Extended-Life Cobalt-Based Superalloys Used in the Manufacturing of Glass Tools; Operational Degradation of Spheroidal Graphite Cast Iron EN GJS SiMo; Structural Changes of Hot Work Tool Steel due to Heat load
- Failure Mechanism of Yttria Stabilized Zirconia Atmospheric Plasma Sprayed Thermal Barrier Coatings Subjected to Calcia-Magnesia-Alumino-Silicate Environmental AttackFailures of Engineering Structures Caused by Weld Imperfections; Fractographical Analysis of Screws Used for Truck Cab Holding; Causal Analysis of Damage of a Cover; Analysis of Damage of Solder Joint of Heat Exchanger; Failure Analysis of Corrugated Hoses; The Influence of Microstructure on the Fracture Development in Engineering Parts; Analysis of the Failure of the Engine Piston of the AlSi Alloy
- Atypical Cases of Welded Structure FailuresAnalysis of Causes of Fractures of Terminal Board Bolts; Chapter 2: Surface Defects and Surface Degradation; Application of Metallography in Solving of Manufacturing Defects of Galvanically Plated Polymers; The Use of Metallography for Examination of Causes of Surface Defects on Visual Parts; Influence of Microstructure on Machinability of Material and its Final Surface Quality; Application of Metallographic Analysis Techniques for Detection and Identification of Spray Paint Defects
- Influence of the Surface Condition of Specimens on the Size of Coherently Diffracting DomainsEvaluation of Titanium Carbonitride Particles Using Image Analysis and Assessment of their Impact on Machinability; Evaluation of Surface Degradation of Deoxidized AW-AlMg0.7Si Alloy; Metallographic Analysis of Filiform Corrosion; Chapter 3: Degradation of Materials and Failure Analysis of Power Equipment; Analysis of Corrosion Attack on Kaplan Turbine Blades; Analysis of Pipeline Serviceability for Water Supply to Power Plant; Development of Creep Damage in Similar Weld Joints of P92 Steel Pipe
- Combining 3D Scanning with Standard Microscopy Methods for Assessment of Pitting Corrosion in Turbine BladesFailure of a Rotating Blade of a 200 MW Steam Turbine LP Rotor and Options for Eliminating other Similar Breakdowns; Quantitative Evaluation of Secondary Phases in a Weld Joint Made of COST F and FB2 Creep Resistant Steels; The Analysis of Causes of the Damage of a Turbine Blade Made of Ti-6Al-4V Alloy; Chapter 4: Analysis of Properties and Production Technologies of Coatings and Non-Ferrous Alloys; Al-Fe Chips Processed by High-Energy Ball Milling and Spark Plasma Sintering